Process of Manufacturing a Medical Use Electrical Lead

ABSTRACT

A process for manufacturing an electrical lead ( 10 ) having one or more electrodes ( 11 ) includes providing an elongate member ( 14 ) having at least one polymeric region and further having at least one electrical conductor ( 13 ) that extends along at least a part of a length of the elongate member ( 14 ) and that is contained in a wall of the elongate member. A length of the at least one electrical conductor ( 13 ) is accessed at the at least one polymeric region ( 34 ). An electrically conductive adhesive ( 15 ) is applied to the length of the at least one electrical conductor ( 13 ) that has been accessed.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application claims priority from U.S. Provisional Patent Application Nos. 60/599,651 filed on 5 Aug. 2004 and 60/648,232 filed on 28 Jan. 2005, the contents of both of which are incorporated herein by reference.

FIELD

This invention relates to the manufacture of an electrical lead and, more particularly, to a process for manufacturing an electrical lead, such as an electrically conductive catheter, and to an electrical lead.

BACKGROUND

The electrical activity of the muscles in the heart directs the overall activity of the heart. Many heart malfunctions, particularly arrhythmias, are evidenced by or caused by electrical activity that is not suitable for the heart's normal functioning. The electrical leads described herein are useful in the detection of the heart's electrical activities and in its treatment by stimulation, ablation and defibrillation.

Electrical leads having electrode regions have been used in the medical field for applications such as those referred to above.

Traditionally, the electrodes have been made from machined metal or coiled wire components which, while having the requisite electrical conductivity, fail to provide the desired degree of flexibility required in a medical application.

Although the use of metal coated or metal filled polymers as medical electrodes has been considered, the amount of metal required to obtain a suitable level of conductivity renders the resultant lead stiff and not particularly suitable for implantation into a patient.

SUMMARY

According to a first aspect of the invention, there is provided a process for manufacturing an electrical lead having one or more electrodes, the process including:

providing an elongate member having at least one polymeric region and further having at least one electrical conductor that extends along at least a part of a length of the elongate member and that is contained in a wall of the elongate member;

accessing a length of the at least one electrical conductor at the at least one polymeric region; and

applying an electrically conductive adhesive to the length of the at least one electrical conductor that has been accessed.

One or more discrete electrodes may be formed along a length of the elongate member. The electrodes may comprise bands that extend at least partially around the circumference of the elongate member.

The electrically conductive adhesive may comprise any of a variety of materials ranging from inherently conductive adhesives, adhesive bases containing solid conductive fillers, adhesive bases containing dissolved conductive materials, and mixtures of these materials. Adhesive bases comprising curable or settable polymeric materials, e.g. polymers that are not tacky or sticky after curing or setting, are also suitable for this purpose. Epoxies containing particulate or fibrillar metals are suitable choices, particularly highly conductive, biocompatible metals such as silver, gold, platinum, palladium, rhodium, and their mixtures as well as alloys containing those metals and constructs of those metals having regions of differing composition. One choice may comprise a silver filled epoxy.

A further step of applying at least one electrically conductive material to the electrically conductive adhesive may be carried out. Again, the electrically conductive material may be any of a variety of materials but particularly suitable are those that are able to form a conductive layer between the conductive adhesive and any additional material placed externally to the at least one electrically conductive material.

One appropriate class of such electrically conductive materials, those that are to be applied to the adhesive, may be a class of liquid carriers, particularly volatile carriers such as solvents, variously containing solvated or complexed conductors or containing solid conductors. A subclass of these materials may be inks containing particulate conductive metals, alloys or constructs such as silver or silver coated with a metal such as platinum or palladium.

The electrically conductive adhesive or the electrically conductive material applied to the electrically conductive adhesive may be further overlaid with a conductive metal such as those described above. The metal may comprise platinum.

The elongate member may include a plurality of electrical conductors and the process may include accessing a length of each of a plurality of the electrical conductors at circumferentially spaced intervals about the elongate member and applying a pad of the electrically conductive adhesive to the accessed length of each electrical conductor.

The process may include applying a layer of at least one electrically conductive material to each pad of electrically conductive adhesive. Further, the process may include overlaying each pad of electrically conductive adhesive with a metal layer including platinum or palladium.

The pads of electrically conductive adhesive may be arranged in longitudinally aligned relationship about the circumference of the elongate member and the process may include applying the metal layer about the circumference of the elongate member as a continuous layer and, thereafter, separating the layer into a plurality of electrically isolated segments, for example, by laser cutting, arranged at circumferentially spaced intervals to form a plurality of discrete electrodes arranged about the circumference of the elongate member.

The process may include applying the metal including platinum by mounting a ring over the elongate member and securing the ring in position. The ring may be secured by adhesive, crimping, or the like.

The electrical lead may include a number of conductors that extend along at least a part of a length of the electrical lead. Although one or more conductors may be specifically associated with an electrode, the electrical lead may include further conductors that form part of a temperature sensing member. A temperature sensing member may be associated with an electrode in such a way that it determines the temperature at said electrode. To determine the temperature at the electrode, the temperature sensing member may be electrically isolated from a corresponding electrode.

The process may, therefore, include the further step of isolating an electrical contact of the electrical lead from said one or more electrodes. The electrical contact may be isolated by:

accessing the electrical contact;

applying an electrically conductive adhesive to the first electrical contact; and

electrochemically treating the electrically conductive adhesive such that a portion of the electrically conductive adhesive is converted to an electrically non-conductive portion.

The electrochemical treatment may include a step of passing a current through the electrical contact such that a current also passes through the electrically conductive adhesive while the electrically conductive adhesive is in an ionic environment containing a material tending to form an insulator (or high resistance layer) with some component of the electrical contact. An ionic environment comprising a saline (NaCl) solution or potassium chloride solution may be suitable, although other such materials are envisaged.

Such a step converts a metal in the electrically conductive adhesive electrochemically to a metal chloride. Where the electrically conductive adhesive comprises a silver filled epoxy, the silver situated on surfaces facing the solution surface is converted to silver chloride. That silver chloride layer may act as an insulating layer.

The electrical contact may comprise a part of a temperature sensing member such as a thermocouple.

According to a second aspect of the invention, there is provided a process of electrically isolating a first electrical contact of an electrical lead from a second electrical contact of the electrical lead, the process including:

accessing the first electrical contact;

applying an electrically conductive adhesive to the first electrical contact; and

electrochemically treating the electrically conductive adhesive such that a portion of the electrically conductive adhesive is converted to an electrically non-conductive portion.

The electrochemical treatment may comprise the step of passing a current through the electrical contact and, hence, through the electrically conductive adhesive to form an insulator. Similarly to the step above, the step may be practised in an ionic environment containing a reactive material to produce an insulator or highly resistive material. In the instance where silver-containing materials are chosen, a saline (NaCl) solution or potassium chloride solution may be suitable.

The electrically conductive adhesive may comprise those listed above, including silver filled adhesives such as a silver filled epoxy. Again, if so chosen, the silver in the portion of the adhesive may be converted to silver chloride (AgCl) using the electrochemical reaction step discussed above. The silver chloride formed is electrically non-conductive.

The first electrical contact may comprise a temperature sensing member.

The second electrical contact may comprise an energy transmitting electrode. The electrode may transmit energy which creates heat in the tissue against which the electrode is placed in use.

The temperature sensing member may be in thermal contact with the energy transmitting electrode.

The temperature sensing member in this variation and others described herein may comprise a thermocouple or other temperature sensing devices such as RTD's, thermistors, or IC devices where the output of frequency or period is related to the temperature. If a thermocouple is chosen, an appropriate choice of conductors may comprise a first wire made of copper and a second wire made of Constantan.

The electrical lead may comprise an elongate member wherein the wires of the thermocouple extend along at least a part of a length of the elongate member and may be contained in a wall of the elongate member. A junction may be formed between the two wires of the thermocouple in proximity to the electrode to form a closed loop thermocouple by the application of the electrically conductive adhesive to the wires to bring the wires into electrical connection with each other at the junction.

At least one electrically conductive material may be applied over the electrode and the thermocouple junction.

Broadly, according to a third aspect of the invention, there is provided a process of manufacturing an electrical lead, the process including:

providing an elongate member having a proximal end and a distal end, at least one electrical conductor contained in the elongate member and extending from the proximal end towards the distal end of the elongate member, the at least one electrical conductor terminating in electrical connection with an electrically conductive zone arranged externally of the elongate member;

cutting the elongate member distally of the electrically conductive zone;

forming a non-conductive termination distally of the electrically conductive zone; and

applying a conductive material over the electrically conductive zone and the termination to form an end electrode of the electrical lead.

More specifically, according to the third aspect of the invention, there is provided a process of manufacturing an electrical lead, the process including:

providing an elongate member having a proximal end and a distal end, the elongate member having one or more polymeric regions and further having a plurality of electrical conductors that extend along at least a part of a length of the elongate member towards the distal end of the elongate member, the electrical conductors being contained within a wall of the elongate member;

in respect of each of at least some of the electrical conductors, forming an electrically conductive zone in electrical contact with its associated electrical conductor by:

accessing a length of each of the at least some electrical conductors through the polymeric region of the elongate member and applying an electrically conductive adhesive to each accessed electrical conductor;

applying conductive material at an access point associated with each electrical conductor to form a plurality of longitudinally spaced electrically conductive zones along the length of the elongate member;

cutting the elongate member distally of one of the electrically conductive zones;

applying an electrically non-conductive termination distally of the one electrically conductive zone; and

applying an electrically conductive material to bridge the electrically conductive zone and the termination to form an end electrode of the elongate member.

The termination may be applied in a liquid state. The termination may be applied in two stages.

Thus, a first layer may be applied to seal the distal end of the elongate member. A second layer may be applied and shaped to provide a desired shape to the end electrode.

The termination may be made from a suitable non-conductive material including a resin. The termination may, particularly, be a synthetic resin such as an epoxy resin.

Instead, the termination may be a solid element which is adhesively secured to the distal end of the elongate member both to seal the end and to form the desired shape of the end electrode.

The desired shape may be a substantially dome shape.

The electrically conductive material may be any of a variety of materials. Preferably, the electrically conductive material is applied in two stages. Firstly, a first layer of an electrically conductive material may be applied in a liquid form. The liquid form may be a liquid carrier, particularly volatile carriers such as solvents, the liquid carrier containing solvated or complexed conductive elements or containing solid conductive elements. A subclass of these materials may be inks containing particulate conductive metals, alloys or constructs such as silver.

As indicated above, the first layer may be applied to the electrically non-conductive termination and to the electrically conductive zone bridging the electrically conductive zone and the termination. This electrically conductive layer may be applied by any suitable means including brushing, dipping, pad printing, or the like.

The layer may be further overlaid with a conductive, biocompatible material such as a suitable metal, for example, platinum.

According to a fourth aspect of the invention, there is provided an electrical lead which includes:

an elongate member having a proximal end and a distal end, at least one electrical conductor contained in the elongate member and extending from the proximal end towards the distal end of the elongate member, the at least one electrical conductor terminating in an electrically conductive zone arranged externally of the elongate member;

a non-conductive termination arranged distally of the electrically conductive zone and at a distal end of the elongate member; and

at least one layer of an electrically conductive material bridging the electrically conductive zone and the non-conductive termination to form an end electrode of the electrically conducive member.

According to a fifth aspect of the invention, there is provided a process of manufacturing an electrical lead, the process including:

providing an elongate member having a proximal end and a distal end, at least one electrical conductor contained in the elongate member and extending from the proximal end towards the distal end of the elongate member, the at least one electrical conductor terminating in electrical connection with an electrically conductive zone arranged externally of the elongate member;

forming an access point in the elongate member to provide access to the at least one electrical conductor;

applying a radio opaque material to a region of the elongate member longitudinally in register with the access point but out of electrical contact with the access point; and

forming the electrically conductive zone by applying at least one layer of an electrically conductive material about the elongate member to be in electrical contact with the conductor through the access point and to overlie the radio opaque material.

According a sixth aspect of the invention, there is provided an electrical lead which includes:

an elongate member having a proximal end and a distal end, at least one electrical conductor contained in the elongate member and extending from the proximal end towards the distal end of the elongate member;

an access point formed at a predetermined location in a wall of the elongate member to provide access to the electrical conductor;

a zone of radio opaque material carried by the elongate member in a region of the elongate member longitudinally in alignment with the access point but circumferentially spaced from the access point; and

at least one layer of an electrically conductive material carried at the predetermined location of the elongate member to provide electrical contact with the electrical conductor through the access point and to overlie the radio opaque material.

The access point may be in the form of a slit arranged transversely in a wall of the elongate member. In this regard, the elongate member may be in the form of a tubular member with a plurality of electrical conductors helically wound, and embedded in, the wall of the elongate member. Therefore, the slit may follow the direction of winding of the electrical conductors.

In one embodiment of this aspect of the invention, the radio opaque material may be a layer of radio opaque material applied to an external surface of the elongate member to form a cuff about the elongate member. The cuff may be in a diametrically opposed position to the access point on the elongate member. The radio opaque material may be applied by pad printing.

Thereafter, the process may including applying the layer of electrically conductive material. The layer of electrically conductive material may comprise a first layer such as the silver ink referred to above. Thereafter, the first layer may be overlaid with a second, biocompatible, electrically conductive material such as platinum.

In another embodiment of this aspect of the invention, the radio opaque material may be inserted into a recess formed in the elongate member. The recess may be formed in a region of the elongate member diametrically opposed to the access point. The recess may be of any suitable shape such as, for example, a slot, a cruciform shape, a circle, or the like. In this embodiment, the conductive layer, may, once again, be applied in two stages. These layers may be applied by pad printing.

The radio opaque material may comprise approximately 70 to 80% non-conductive material and about 20 to 30% of adhesive material.

The adhesive material may comprise an epoxy. Preferably, the epoxy of the radio opaque material is matched to that of the silver ink to facilitate pad printing.

In the case where the radio opaque material is contained within a recess in the elongate member, the epoxy of the radio opaque material may be selected to be the same as that used in filling the access point. This is advantageous for biocompatibility purposes.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows, schematically, a partially sectioned side view of an electrical lead in accordance with an embodiment of the invention;

FIGS. 2 a to 2 f show, schematically, steps of a process, in accordance with an embodiment of the invention, for manufacturing the electrical lead of FIG. 1;

FIG. 3 shows, schematically, the electrical lead after completion of the process;

FIG. 4 shows a schematic, sectional end view of an electrical lead manufactured in accordance with a process of another embodiment of the invention;

FIG. 5 shows a schematic, side view of a part of an electrical lead manufactured in accordance with a process of yet another embodiment of the invention;

FIGS. 6 a to 6 d show, schematically, steps of a process, in accordance with a further embodiment of the invention, of electrically isolating a first electrical contact of an electrical lead from a second electrical contact of the electrical lead;

FIGS. 7 a to 7 e show, schematically, steps of a process, in accordance with yet a further embodiment of the invention, for manufacturing an electrical lead;

FIG. 8 shows, schematically, a three dimensional view of an initial step of a process, in accordance with still a further embodiment of the invention, for manufacturing an electrical lead;

FIG. 9 shows a schematic, sectional end view of a first example of an electrical lead manufactured in accordance with the still further process of manufacturing an electrical lead;

FIG. 10 shows a schematic, sectional end view of a second example of an electrical lead manufactured in accordance with the still further process of manufacturing an electrical lead; and

FIGS. 11 a to 11 d show, schematically, variations of the example of the electrical lead shown in FIG. 9.

DETAILED DESCRIPTION OF EXEMPLARY EMBODIMENT

Referring to the drawings, an electrical lead made in accordance with a process for manufacturing an electrical lead, in accordance with an embodiment of the invention, is generally designated by the reference numeral 10.

The electrical lead 10 comprises an elongate member 10 a carrying at least one electrode 11 and, preferably, a number of band electrodes 11 positioned at longitudinally spaced intervals along the length of the elongate member 10 a. An electrode not in the shape of a band is shown as 11 b.

FIG. 3 shows a side view of the resulting electrical lead 10 functioning as an electrode sheath of a catheter and extending from an introducer 30 or a similar device. The lead 10 includes a plurality of longitudinally spaced electrodes 11, at least some of the electrodes 11 being band electrodes

As described in the preceding paragraph, the electrical lead 10 is used as the electrode sheath of a cardiac catheter. The electrodes 11 are used as sensing electrodes to sense electrical activity (whether normal or not) in the muscles of the heart. In addition, the electrodes 11 may be used to ablate an area of tissue in the heart to correct some anomaly.

Thus, each electrode 11 may initially be operable as a sensing electrode. Such an electrode 11 enables a clinician to identify an area of electrical disturbance in the heart of a patient. The electrical disturbance may be caused by a damaged area of heart tissue that is “mis-firing”. Once located, the same electrode 11 may be switched to an ablation function to ablate the damaged tissue.

Multi-function electrodes 11 may be particularly useful in the treatment of atrial fibrillation. Atrial fibrillation, a cardiac arrhythmia, results when an area of cardiac tissue near the atrium “misfires”. Such misfiring causes an electrical disturbance in the normal electrical pathway and in the resultant pulsatile contraction of the atrium. The result is that the atrium contracts in a fast and disorganised manner. If the fibrillation is prolonged, the blood in the atrium is not fully emptied into the ventricle leading to a number of complications. By sensing the area of tissue that is causing the electrical disturbance, the precise area may then be ablated.

Production of the electrical lead 10 is shown in FIGS. 2 a to 2 f. Initially, as shown in FIG. 2 a, an inner member 12 made from a suitable polymer such as polyethylene or polyether block amide (PEBAX) is provided. Other polymeric materials are also acceptable and easily identified from the art.

As shown in FIG. 2 b, a plurality of conductors 13 are coiled in a helical manner around an outer surface of the inner member 12. Alternatively, the conductors 13 are housed within a lumen of the inner member 12. Up to 24 or more conductors 13 may be used in the electrical lead 10 and are either helically wound around or are situated within the lumen of the inner member 12.

The conductors 13 are metal wires. The metal wires are insulated with a polymeric material such as Nylon, polyurethane or a nylon-polyurethane co-polymer. Examples of suitable conductors include copper or Constantan coated with a Nylon-polyurethane blend.

As shown in FIG. 2 c, an outer polymeric jacket 14 is formed, for example, by extrusion, over the inner member 12 and the conductors 13 to form the elongate member 10 a. The outer polymeric jacket 14 is made from materials similar to or the same as the materials of the inner member 12. Other materials may be selected as a matter of design choice, however.

The elongate member 10 a comprising the inner member 12, the conductors 13 and the outer polymeric jacket 14 is heat treated to secure the outer polymeric jacket 14 to the inner member 12 and to the conductors 13. It will be appreciated that a wall of the electrical lead 10 is therefore effectively made up of an inner layer defined by the inner member 12, a central layer made up of the helically wound conductors 13 and an outer layer defined by the outer jacket 14. The conductors 13 are, in effect, embedded in the wall and, as there is little, if any, polymeric material between adjacent turns of the conductors 13, there is the ability for limited movement between adjacent turns thereby improving the flexibility of the electrical lead 10.

As shown in FIG. 2 d, a desired length of one or more conductors 13 is accessed or exposed by laser cutting a portion of the outer jacket 14. Laser cutting is accurate and provides a suitable way of removing a portion 32 of the outer polymeric jacket 14 with ease to produce an opening 34. The area 34 of the outer polymeric jacket that has been removed is of a width similar to the width of the exposed conductors 13 and of a selected length extending along a predetermined length of the conductors 13, following the coiled or helical path of the conductors 13. The amount of outer polymeric jacket 14 that is removed largely depends upon the requirements of the final electrode 11. For example, there may be instances where it is desired to expose two or more adjacent conductors 13 to provide an electrode 11 with increased electrical conductivity and increased mechanical strength.

If the conductors 13 are insulated, the step of exposing the conductor(s) also cuts and removes the layer of insulation over the wires in addition to cutting and removing a corresponding portion of the outer polymeric jacket 14.

As shown in FIG. 2 e, the opening 34 formed in the outer polymeric jacket 14 is substantially filled with an electrically conductive adhesive 15 of the types discussed above such as a silver filled epoxy. The conductors 13 coated with the electrically conductive adhesive 15 provide sufficient electrical conductivity to act as an electrode 11. Such an electrode 11 has particular application as a sensing electrode.

However, as shown in FIG. 2 f, the process, preferably, further comprises a step of covering the electrically conductive adhesive 15 with a solvent that contains one or more conductive materials. The class of suitable materials is discussed above. These materials may be applied in a variety of ways, e.g., spraying, electrostatic deposition, direct application as by brush or pad, or the like. Good results are obtained using pad printing with silver filled ink or palladium filled ink or a palladium/silver ink 16.

Electrodes 11 formed in this manner, by pad printing an electrically conductive adhesive 15 with an electrically conductive ink 16, have a particular application as sensing electrodes. The process also includes a further step of catalysing the pad printed ink 16 with an acidic palladium chloride solution to deposit a coating of palladium on the silver of the electrode.

The electrically conductive adhesive 15 or the pad printed coating of ink 16 is overlaid with a layer of platinum 17 to increase the electrical conductivity across the electrode. An electrode 11 that includes a layer of platinum 17 is suitable for ablation in addition to sensing. The platinum 17 is applied to the electrode 11 by electroless plating but could also be applied by electrode deposition techniques.

The final electrode 11 may also be coated with a layer of material appropriate for prevention of metallic ions from the electrodes. An epoxy layer may be applied by pad printing. The epoxy prevents the migration of silver ions from the electrode 11.

In FIG. 4 of the drawings where, with reference to previous drawings, like reference numerals refer to like parts unless otherwise specified, another embodiment of the invention is illustrated. In this embodiment, a plurality of the electrical conductors 13 are accessed through excising a plurality of the portions 32 (not shown in FIG. 4 but shown in FIG. 2 d) at circumferentially spaced intervals about the outer jacket 14 to form a plurality of circumferentially spaced openings 34. While FIG. 4 illustrates the openings 34 being in longitudinal alignment, it will be appreciated that the openings 34 could be staggered with respect to one another along the length of the outer jacket 14.

Each opening 34 is charged with the conductive adhesive 15 and the layer 16 of electrically conductive material is pad printed about the circumference of the outer jacket 14 overlying the conductive adhesive 15 in each of the openings 34. The biocompatible metal layer 17 is applied over the layer 16 of electrically conductive material.

Once the metal layer 17 has been applied, laser cuts 19 are made through the layers 16 and 17 to form a plurality of circumferentially spaced discrete electrodes 11. It will be appreciated that it is an advantage of this embodiment of the invention, that three-dimensional sensing or ablating can be effected. Also, it is easier to place the catheter 10 as the orientation of the electrodes 11 of the catheter 10 relative to a site of a patient's body to be treated is less critical as there is always likely to be at least one electrode 11 in contact with tissue.

Referring now to FIG. 5 of the drawings, yet a further embodiment of the invention is described. Once again, with reference to the previous drawings, like reference numerals refer to like parts unless otherwise specified.

In this embodiment, instead of the layer 17 of each electrode 11 being pad printed, a ring 60 is applied over the layer 16. The ring 60 is secured in position on the outer jacket 14 over its associated layer 16 by an appropriate securing technique, for example, an adhesive, crimping, being a press fit, or the like.

It is also useful to measure the temperature at an electrode 11, particularly in cases where the electrode 11 is used for ablation purposes. The electrical lead 10, therefore, includes a thermocouple 20 (FIG. 6 b) or other suitable temperature measuring component.

As shown in FIG. 6 a, in a variation including the thermocouple 20, the thermocouple 20 comprises a first wire 21 made from copper and a second wire 22 made from Constantan. The outer polymeric jacket 14 is cut, for example, by laser cutting, to expose the wires 21 and 22. An electrically conductive adhesive 15 is applied to the exposed wires as shown in FIG. 6 b. The electrically conductive adhesive 15 brings the two wires 21 and 22 of the thermocouple 20 into electrical contact with each other thus providing a thermocouple junction 23.

When forming the thermocouple 20 in this way and to ensure accurate temperature readings, the thermocouple 20 needs to be isolated from an associated electrode 11 as described in the steps below. As shown in FIG. 6 c, after the wires 21 and 22 of the thermocouple 20 are exposed and the electrically conductive adhesive 15 has been applied to the exposed wires 21 and 22, the wires and adhesive are exposed to a saline (NaCl) solution 24 and a current is passed through the wires 21 and 22 of the thermocouple 20 from a constant voltage source 26. The resultant current passing through the adhesive 15 causes a metal in the adhesive to convert to a metal chloride. When the adhesive 15 is a silver filled epoxy, the silver on an outer facing surface of the adhesive is converted to a relatively thin layer 25 of silver chloride and acts as a layer of insulation, electrically isolating the thermocouple 20 from the electrode 11 of the electrical lead 10.

As shown in FIG. 6 d, the adhesive 15 of the electrode 11 and the adhesive 15 of thermocouple 20 are then pad printed with a silver filled ink 16 and a layer of platinum 17 is, optionally, applied to the ink 16.

The electrical lead 10 may comprise a single thermocouple 20 or, alternatively, a number of thermocouples. In the latter case, each electrode 11 formed on the electrical lead 10 may have a corresponding thermocouple 20.

EXAMPLE

A cable was sourced from Microhelix, Portland, Oreg. The cable had been prepared by extruding a PEBAX jacket over a polymer coated wire mandrel. A mixture of Nylon/polyurethane insulated copper and Constantan wires (each 0.125 mm) were helically coiled around the polymer coated wire mandrel at a controlled pitch/coiling angle. The PEBAX jacket was then laid over the coiled wires. The resultant cable was cut to length and the mandrel removed. The cable was then heat treated to secure the outer PEBAX jacket to the coiled wires.

Excimer laser cut windows were then cut over the individual wires at pre-determined locations. The exact locations of the windows were programmed into the laser. The outer PEBAX jacket over the individual wire together with the insulation layer of the wire were removed without disturbing the wire beneath.

The openings formed by removal of the regions of PEBAX and insulation were filled with a silver filled epoxy from Creative Materials using an air actuated dispenser. The silver filled epoxy was cured at a temperature of about 140° C. and subsequently plasma treated in an argon atmosphere for approximately 1 min.

The silver filled epoxy regions were then pad printed with a silver filled ink. A plate with indentations relating to the size and spacing of the desired electrodes was wiped with the silver filled ink, leaving ink behind in the indentations. A pad was then brought down over the top of the plate along the length of the ink filled wells. The pad picked up the ink and was placed on the cable such that the ink pads corresponded with the regions of epoxy on the cable to deposit the ink on the cable over the regions of epoxy. This step was repeated a number of times as the cable was rotated such that a series of bands were formed around the circumference of the cable.

The cable was then cured in an oven at about 140° C. for up to 15 hours.

The bands of the cable were then further catalysed with an acidic PdCl solution.

Finally, the cable was placed in a commercially available electroless Pt solution using hydrazine as the reducer for approximately 1 hour at about 60° C. A layer of platinum approximately 0.5 microns in thickness was formed over the bands to form final band electrodes.

Referring to FIGS. 7 a to 7 e of the drawings, a further embodiment of a process for manufacturing an electrical lead 10 is described. With reference to the previous drawings, like reference numerals refer to like parts unless otherwise specified.

In this embodiment of the invention, the electrodes 11 are formed at spaced intervals along a length of the elongate member 10 a to be in electrical communication with the underlying conductors 13 (not shown in FIGS. 7 a-7 e).

The elongate member 10 a is cut at a distal end 40, as shown in FIG. 7 a of the drawings, distally of one of the electrodes 11.

A layer of an epoxy 42 is applied at the distal end 40 of the elongate member 10 a to seal the distal end of the elongate member 10 a and to isolate the ends of the conductors at the distal end 40. A further bead of epoxy 44 is applied to the layer 42 to form an end electrode of a required dome shape 46.

In a following step, the shaped end 46 is coated with conductive silver ink of the same formulation as that used in the formation of the electrodes 11 as shown in FIG. 7 d of the drawings. It will therefore be appreciated that the end electrode 46 is formed prior to the application of the platinum layer on the electrodes 11.

Therefore, once the shaped end 46 has been coated with the silver ink, all of the electrodes 11 and the end electrode 48 are coated with a layer of platinum 17 as shown in FIG. 7 e of the drawings. Once again, the platinum layer 17 is applied by electroless plating.

Referring now to FIGS. 8 to 11 of the drawings, yet a further process for manufacturing an electrical lead 10 is illustrated. Once again, with reference to the previous drawings, like reference numerals refer to like parts, unless otherwise specified.

In this embodiment, prior to the formation of the electrodes 11 about the outer jacket 14, once each opening 34 has been formed in the outer jacket 14, a radio opaque material 50 is applied longitudinally in register with each of at least some of the openings 34.

In the case of the embodiment shown in FIGS. 8 and 9 of the drawings, the radio opaque material 50 is applied in the form of a cuff 52 about a part of the circumference of the outer jacket 14.

The cuff 52 is arranged on the jacket 14 so that it is at the same longitudinal position on the jacket 14 as its associated opening 34 but is arranged in diametrically opposed relationship to the opening 34 so that the radio opaque material 50 is not in electrical contact with the conductor 13 or the electrically conductive adhesive 15 in the opening 34.

The radio opaque material 50 is applied by pad printing and comprises between 70 to 80% non-conductive material and 20 to 30% adhesive. The radio opaque material is a radio opaque ink sourced from Creative Materials of 141 Middlesex Road, Tyngsboro, Mass., 01879, United States of America. The adhesive part of the radio opaque material is, conventionally, an epoxy. The epoxy of the radio opaque material 50 is matched to the epoxy of the silver layer 16 which is advantageous for biocompatibility purposes.

Once the radio opaque material 50 has been applied, the layer of electrically conductive silver material 16 is pad printed to overlie the radio opaque material and the adhesive 15 in the opening 34. Thereafter, the platinum layer 17 is applied by electroless plating.

In the embodiment shown in FIGS. 10 and 11 of the drawings, instead of applying the radio opaque material 50 as a cuff 52, a recess 54 is formed in the outer jacket 14 in diametrically opposed relationship to the opening 34. It will be appreciated that the recess 54 is of such a depth that it does not expose any of the conductors 13 in the outer jacket 14.

The radio opaque material 50 is charged into the recess 54. In this embodiment, the epoxy of the radio opaque material is selected to be the same as the epoxy used to form the electrically conductive filling 15 of the opening 34. Once again, this is advantageous for biocompatibility purposes.

The recess 54 can be any suitable shape. Thus, as shown in FIG. 11 a of the drawings, the recess 54 may be a longitudinally extending slit. Instead, as shown in FIGS. 11 b and 11 c of the drawings, the recess 54 could be of a cruciform shape. As shown in FIG. 11 d of the drawings, the recess could be a circular recess. It will be appreciated that any other shape of recess could equally advantageously be employed.

Once the recess 54 contains the radio opaque material 50, the silver ink 16 is applied by pad printing followed by the electroless plating of the electrode 11 with a platinum layer 17.

It will be appreciated that the silver ink layer 16 or the platinum layer 17 need not extend over the radio opaque material 52 or 54, as the case may be. It is only necessary that the radio opaque material 52 or 54 be longitudinally aligned with its associated electrode 11.

It is an advantage of this embodiment that a radio opaque region is formed in alignment with the electrode 11 allowing for rapid and accurate placement of the electrode 11 by a clinician viewing the position of the electrode 11 on a fluoroscope.

It will be appreciated by persons skilled in the art that numerous variations and/or modifications may be made to this described process without departing from the spirit or scope of the broadly description. The specific descriptions are, therefore, to be considered in all respects as illustrative and not restrictive. 

1. A process for manufacturing a medical use electrical lead having one or more electrodes, the process including: providing an elongate member having at least one polymeric region and further having at least one electrical conductor that extends along at least a part of a length of the elongate member and that is contained in a wall of the elongate member; accessing a length of the at least one electrical conductor at the at least one polymeric region; and; applying an electrically conductive adhesive to the length of the at least one electrical conductor that has been accessed.
 2. The process of claim 1 in which the electrically conductive adhesive comprises a silver filled epoxy.
 3. The process of claim 2 in which at least some of the silver particles of the silver filled epoxy are coated with platinum or palladium.
 4. The process of claim 1 which includes applying at least one electrically conductive material to the electrically conductive adhesive.
 5. The process of claim 1 which includes overlaying the electrically conductive adhesive with a metal including platinum.
 6. The process of claim 4 which includes overlaying the electrically conductive material with a metal including platinum.
 7. The process of claim 1 in which the elongate member includes a plurality of electrical conductors and in which the process includes accessing a length of each of a plurality of the electrical conductors at circumferentially spaced intervals about the elongate member and applying a pad of the electrically conductive adhesive to the accessed length of each electrical conductor.
 8. The process of claim 7 which includes applying a layer of at least one electrically conductive material to each pad of electrically conductive adhesive.
 9. The process of claim 7 which includes overlaying each pad of electrically conductive adhesive with a metal layer including platinum or palladium.
 10. The process of claim 9 in which the pads of electrically conductive adhesive are arranged in longitudinally aligned relationship about the circumference of the elongate member and in which the process includes applying the metal layer about the circumference of the elongate member as a continuous layer and, thereafter, separating the layer into a plurality of electrically isolated segments arranged at circumferentially spaced intervals to form a plurality of discrete electrodes arranged about the circumference of the elongate member.
 11. The process of claim 6 which includes applying the metal including platinum by mounting a ring over the elongate member and securing the ring in position.
 12. The process of claim 1 which includes isolating an electrical contact of the electrical lead from said one or more electrodes by: accessing the electrical contact; applying an electrically conductive adhesive to the first electrical contact; and electrochemically treating the electrically conductive adhesive such that a portion of the electrically conductive adhesive is converted to an electrically non-conductive portion.
 13. The process of claim 12 in which electrochemically treating the electrically conductive material comprises passing a current through the electrical contact in an ionic environment.
 14. The process of claim 13 in which the ionic environment comprises a saline (NaCl) solution to convert a metal in the electrically conductive adhesive electrochemically to a metal chloride.
 15. The process claim 12 in which the electrical contact is a contact of a thermocouple junction.
 16. A process of electrically isolating a first electrical contact of a medical use electrical lead from a second electrical contact of the electrical lead, the process including: accessing the first electrical contact; applying an electrically conductive adhesive to the first electrical contact; and electrochemically treating the electrically conductive adhesive such that a portion of the electrically conductive adhesive is converted to an electrically non-conductive portion.
 17. The process of claim 16 in which the electrochemical treatment comprises the step of passing a current through the electrical contact in an ionic environment.
 18. The process of claim 17 in which the ionic environment comprises a saline (NaCl) solution to convert a metal in the electrically conductive adhesive electrochemically to a metal chloride.
 19. The process of claim 16 in which the first electrical contact comprises a temperature sensing member.
 20. The process of claim 16 in which the second electrical contact comprises an energy transmitting electrode.
 21. The process of claim 20 in which the temperature sensing member comprises a thermocouple, the thermocouple having a first wire made of copper and a second wire made of Constantan.
 22. A process of manufacturing a medical use electrical lead, the process including: providing an elongate member having a proximal end and a distal end, at least one electrical conductor contained in the elongate member and extending from the proximal end towards the distal end of the elongate member, the at least one electrical conductor terminating in electrical connection with an electrically conductive zone arranged externally of the elongate member; cutting the elongate member distally of the electrically conductive zone; forming a non-conductive termination distally of the electrically conductive zone; and applying a conductive material over the electrically conductive zone and the termination to form an end electrode of the electrical lead.
 23. A process of manufacturing a medical use electrical lead, the process including: providing an elongate member having a proximal end and a distal end, the elongate member having one or more polymeric regions and further having a plurality of electrical conductors that extend along at least a part of a length of the elongate member towards the distal end of the elongate member, the electrical conductors being contained within a wall of the elongate member; in respect of each of at least some of the electrical conductors, forming an electrically conductive zone in electrical contact with its associated electrical conductor by: accessing a length of each of the at least some electrical conductors through the polymeric region of the elongate member and applying an electrically conductive adhesive to each accessed electrical conductor; applying conductive material at an access point associated with each electrical conductor to form a plurality of longitudinally spaced electrically conductive zones along the length of the elongate member; cutting the elongate member distally of one of the electrically conductive zones; applying an electrically non-conductive termination distally of the one electrically conductive zone; and applying an electrically conductive material to bridge the electrically conductive zone and the termination to form an end electrode of the elongate member.
 24. The process of claim 22 which includes applying the termination in a liquid state.
 25. The process of claim 24 which includes applying the termination in two stages, a first layer being applied to seal the distal end of the elongate member and a second layer being applied and shaped to provide a desired shape to the end electrode.
 26. The process of claim 22 which includes applying a solid termination to the distal end of the elongate member.
 27. The process of claim 22 which includes applying the electrically conductive material in two stages.
 28. The process of claim 27 which includes applying a first layer to the electrically non-conductive termination and to the electrically conductive zone bridging the electrically conductive zone and the termination.
 29. The process of claim 28 which includes overlaying the first layer with a conductive, biocompatible material.
 30. A medical use electrical lead which includes: an elongate member having a proximal end and a distal end, at least one electrical conductor contained in the elongate member and extending from the proximal end towards the distal end of the elongate member, the at least one electrical conductor terminating in electrical connection with an electrically conductive zone arranged externally of the elongate member; a non-conductive termination arranged distally of the electrically conductive zone and at a distal end of the elongate member; and at least one layer of an electrically conductive material bridging the electrically conductive zone and the non-conductive termination to form an end electrode of the electrically conducive member.
 31. The lead of claim 30 in which the termination is made from a non-conductive material including a resin.
 32. The lead of claim 31 in which the termination is a synthetic resin.
 33. The lead of claim 30 in which the termination is a solid element which is adhesively secured to the distal end of the elongate member both to seal the end and to form a desired shape for the end electrode.
 34. A process of manufacturing a medical use electrical lead, the process including: providing an elongate member having a proximal end and a distal end, at least one electrical conductor contained in the elongate member and extending from the proximal end towards the distal end of the elongate member, the at least one electrical conductor terminating in electrical connection with an electrically conductive zone arranged externally of the elongate member; forming an access point in the elongate member to provide access to the at least one electrical conductor; applying a radio opaque material to a region of the elongate member longitudinally in register with the access point but out of electrical contact with the access point; and forming the electrically conductive zone by applying at least one layer of an electrically conductive material about the elongate member to be in electrical contact with the conductor through the access point and to overlie the radio opaque material.
 35. The process of claim 34 which includes applying the radio opaque material as a layer to an external surface of the elongate member to form a cuff about the elongate member.
 36. The process of claim 35 which includes positioning the cuff in a diametrically opposed position to the access point on the elongate member.
 37. The process of claim 36 which includes applying the layer of electrically conductive material over the cuff, the layer of electrically conductive material comprising a first conductive layer overlaid with a second, biocompatible, electrically conductive material layer.
 38. The process of claim 34 which includes inserting the radio opaque material into a recess formed in the elongate member, the recess being formed in a region of the elongate member diametrically opposed to the access point.
 39. A medical use electrical lead which includes: an elongate member having a proximal end and a distal end, at least one electrical conductor contained in the elongate member and extending from the proximal end towards the distal end of the elongate member; an access point formed at a predetermined location in a wall of the elongate member to provide access to the electrical conductor; a zone of radio opaque material carried by the elongate member in a region of the elongate member longitudinally in alignment with the access point but circumferentially spaced from the access point; and at least one layer of an electrically conductive material carried at the predetermined location of the elongate member to provide electrical contact with the electrical conductor through the access point and to overlie the radio opaque material.
 40. The lead of claim 39 in which the access point is in the form of a slit arranged transversely in a wall of the elongate member, the slit following the direction of winding of the electrical conductors.
 41. The lead of claim 39 in which radio opaque material comprises approximately 70 to 80% non-conductive material and about 20 to 30% of adhesive material.
 42. The lead of claim 41 in which the adhesive material comprises an epoxy.
 43. The lead of claim 41 in which the radio opaque material is applied as a layer about a part of the circumference of the elongate member.
 44. The lead of claim 43 in which the epoxy of the adhesive material of the radio opaque material is matched to that of the layer of the electrically conductive material.
 45. The lead of claim 42 in which the radio opaque material is contained within a; recess in the elongate member, the recess being arranged in a diametrically opposed position relative to the access point.
 46. The lead of claim 45 in which the epoxy of the radio opaque material is selected to be the same as that used in filling the access point.
 47. The process of claim 10 which includes applying the metal including platinum by mounting a ring over the elongate member and securing the ring in position.
 48. The process of claim 23 which includes applying the termination in a liquid state.
 49. The process of claim 48 which includes applying the termination in two stages, a first layer being applied to seal the distal end of the elongate member and a second layer being applied and shaped to provide a desired shape to the end electrode.
 50. The process of claim 23 which includes applying a solid termination to the distal end of the elongate member.
 51. The process of claim 23 which includes applying the electrically conductive material in two stages.
 52. The process of claim 51 which includes applying a first layer to the electrically non-conductive termination and to the electrically conductive zone bridging the electrically conductive zone and the termination.
 53. The process of claim 52 which includes overlaying the first layer with a conductive, biocompatible material. 